OUR PRODUCTS
TIOMIX
TIOMIX
TIOMIX is a 2-component sealant of cold hardening developed on polysulfide based polymer and hardened by classical reaction of interaction of end SH-group with manganese dioxide.
form PRODUCT REQUEST FORM

DESCRIPTION

TIOMIX is a 2-component sealant of cold hardening developed on polysulfide based polymer and hardened by classical reaction of interaction of end SH-group with manganese dioxide.

TIOMIX is delivered in the form of a set consisting of component A (base) and component B (hardener) mixed just before application. After mixing of components, the sealant forms thixotropic and easily applied paste.

After hardening as result of chemical reaction the elastic rubber-like material with high strength properties, resistance to vibrations and atmospheric actions is formed, it has excellent adhesion to surfaces ranging from glass, aluminum to stainless and zinc galvanized steel.

AREA OF APPLICATION


TIOMIX is a secondary perimeter sealant for production of insulation glass units providing its mechanical strength, protecting primary sealant and ensuring an additional barrier for penetration of water moisture inside insulation glass unit and diffusion of gases.


ADVANTAGES

The sealant has the following distinctive properties:
high adhesion to glass, metal and plastic spacers (aluminum, stainless or zinc galvanized steel, PVC);
optimal physical and mechanical properties both for automatic and hand application;
optimal pot life and hardening time;
optimal thixotropic properties (no leaks, no stringing);
high resistance to atmospheric impact and heat-aging resistance.

 

 

 

Name of an indicator

 

THIOMIX for manual application

 

THIOMIX for automatic (extruder) application

1. External appearance

 

 

- component A

White to beige colored paste

White to beige colored paste

- component B

Black-colored paste

Black-colored paste

2. Viscosity at 23°C

 

 

- Component A, spz

(230 – 280)*1000

(250 – 300)*1000

- Component B, spz

(80 – 120)*1000

(80 – 120)*1000

3. Density at 23°C

 

 

- component A, g/cm3

1,85-1,95

1,8-1,9

- component B, g/cm3

1,5-1,6

1,5-1,6

4. Pot life at 23°C (primary hardening), minutes

30 - 60

30 - 60

5. Resistance to fluidity (thixotropy), mm, no more

2

2

6. Degree of curing (hardness), Shore A unit:

 

 

- in 2 h at 23°C, not less

25

25

- in 24h at 23°C, not less

35

40

7. Adhesion to glass, min., not less

10

10

8. Adhesion to a remote frame, min., not less

10

10

9. Nature of destruction

cohesive

cohesive

10. Conditional tensile strength at break, MPa, not less

0.5

0.7

11. Specific elongation at break, %, not less

50

50

12. Degree of grinding of component B, micron, no more

50

50


METHOD OF APPLICATION

TIOMIX component A shall be used only with TIOMIX component B. For a dosage of components, preparation and application of the sealant mixture, it is necessary to use the special equipment or tools.

Pot life of the sealant ranges from 30 to 60 min. depending on a batch of the sealant, mixing ratio of components and environmental conditions.


MIXING RATIO A:B

10:1 by volume
10:0,9 by weight

The sealant mixture shall be prepared according to proportions indicated on the sealant’s labels and according to information of technical data sheet

Ambient temperature makes considerable effect on curing speed of the sealant.


STORAGE

Components of the sealant should be stored in the closed dry conditions protected from direct sun, atmospheric precipitation and mechanical damages.

The recommended storage temperature: +10°C …+30°C.

 

 